Phase-field-method-studied mechanism of Cu-rich phase precipitation in Al<sub><i>x</i></sub>CuMnNiFe high-entropy alloy

姓名
邮箱
手机号码
标题
留言内容
验证码

Abstract

High-entropy alloys with BCC and FCC coexisting structures usually have excellent comprehensive mechanical properties, and Al element can promote the transformation of Cu-containing high-entropy alloys from FCC structure to BCC structure to obtain the BCC and FCC coexisting structures. In order to illustrate the process of phase separation of high entropy alloys, a low-cost Al-TM transition group element high-entropy alloy is selected in this work. Based on the Chan-Hilliard equation and Allen-Cahn equation, a three-dimensional phase field model of Al _xCuMnNiFe high-entropy alloy is established, and the microscopic evolution of the nano-Cu-rich phase of Al _xCuMnNiFe high-entropy alloy ( x= 0.4, 0.5, 0.6, 0.7) at 823 K isothermal aging is simulated. The results show that the Al _xCuMnNiFe high-entropy alloy generates two complex core-shell structures upon aging: Cu-rich core/B2 _sshell and B2 _ccore/FeMn shell, and it is found through discussion and analysis that the formed B2 _cplays an inhibitory role in the formation of the nano-Cu-rich phase, and that this inhibitory role becomes larger with the increase of Al element. Combining the empirical formula, the curve of yield strength of the Cu-rich phase varying with the aging time is obtained for the Al _xCuMnNiFe high-entropy alloy, and the overall yield strength of the high-entropy alloy has a rising-and-then-falling trend with the change of time, and the aging time of the peak yield strength and the alloy system are obtained from the change of the curve, so that the best alloy system and aging time of the high-entropy alloy can provide a reference for aging process.

Keywords:

Authors and contacts

Corresponding author:Zhao Yu-Hong,zhaoyuhong@nuc.edu.cn

Funds:Project supported by the National Natural Science Foundation of China (Grant Nos. 52074246, 22008224, 52275390, 52205429, 52201146), the National Defense Basic Scientific Research Program of China (Grant Nos. JCKY2020408B002, WDZC2022-12), the Key Research and Development Program of Shanxi Province (Grant Nos. 202102050201011, 202202050201014), and the Shanxi Graduate Innovation Project, China (Grant No. 2021Y592)

FullText HTML: translate this paragraph

References

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]
[36]
[37]
[38]
[39]
[40]
[41]
[42]
[43]
[44]
[45]
[46]
[47]
[48]
[49]
[50]
[51]
[52]
[53]
[54]
[55]
[56]
[57]
[58]
[59]
[60]
[61]
[62]
[63]
[64]
[65]
[66]
[67]
[68]

Cited By

DownLoad: Full-Size Img PowerPoint

Alloy system	Al	Cu	Mn	Ni	Fe
Al_0.4Cu_1.5Mn₁Ni₁Fe_1.5	7.4	27.8	18.5	18.5	27.8
Al_0.5Cu_1.5Mn₁Ni₁Fe_1.5	9.2	27.2	18.2	18.2	27.2
Al_0.6Cu_1.5Mn₁Ni₁Fe_1.5	10.8	26.8	17.8	17.8	26.8
Al_0.7Cu_1.5Mn₁Ni₁Fe_1.5	12.28	26.36	17.5	17.5	26.36

DownLoad: CSV

Alloy elements		Cu	Mn	Ni	Al
${D}_{i}^{0, \varphi }/{({10}^{-5}~{\rm{m} } }^{2}{\cdot}{ {\rm{s} } }^{-1}$)	${\rm{\alpha } }({\rm{B} }{\rm{C} }{\rm{C} })$	4.70	14.90	14.00	53.50
	${\rm{\gamma } }({\rm{F} }{\rm{C} }{\rm{C} })$	4.30	1.78	1.08	2.20
${Q}_{i}^{0, \varphi }/{({10}^{5}~{\rm{J} }{\cdot}{\rm{m} }{\rm{o} }{\rm{l} } }^{-1}$)	${\rm{\alpha } }({\rm{B} }{\rm{C} }{\rm{C} })$	2.44	2.63	2.64	2.71
	${\rm{\gamma } } ({\rm{F} }{\rm{C} }{\rm{C} } )$	2.80	2.64	2.73	2.67
$ {D}_{i}^{0, \varphi } $-frequency factor; $ {Q}_{i}^{0, \varphi } $-diffusion activation energy

DownLoad: CSV

Parameter type	Parameter	Value	Unit
Cahn-Hilliard model^[55]	$ {\kappa }_{c} $	$ 5.0\times {10}^{-15} $	${\rm{J} \cdot}{ {\rm{m} } }^{2}{\cdot{\rm{m} }{\rm{o} }{\rm{l} } }^{-1}$
	$ {\kappa }_{\eta } $	$ 1.0\times {10}^{-15} $	$ {\rm{J}}{\cdot{\rm{m}}}^{2}{\cdot{\rm{m}}{\rm{o}}{\rm{l}}}^{-1} $
	$ Y $	$ 2.14\times {10}^{11} $	$ {\rm{P}}{\rm{a}} $
	$ {V}_{{\rm{m}}} $	$ 7.09\times {10}^{-6} $	${ {\rm{m} } }^{3}{\cdot {\rm{m} }{\rm{o} }{\rm{l} } }^{-1}$
	$ W $	$ 5.0\times {10}^{3} $	${\rm J} {\cdot} {\rm mol}^{-1}$
	$ T $	823	K
Elasticity constant^[56]	$ {C}_{11}^{{\rm{m}}} $	228	GPa
	$ {C}_{12}^{{\rm{m}}} $	132	GPa
	$ {C}_{44}^{{\rm{m}}} $	116.5	GPa
	$ {C}_{11}^{{\rm{p}}} $	169	GPa
	$ {C}_{12}^{{\rm{p}}} $	122	GPa
	$ {C}_{44}^{{\rm{p}}} $	75.3	GPa
Lattice misfit coefficient^[55]	$ {\varepsilon }_{{\rm{C}}{\rm{u}}}^{0} $	$ 3.29\times {10}^{-2} $
	$ {\varepsilon }_{{\rm{M}}{\rm{n}}}^{0} $	$ 5.22\times {10}^{-4} $
	$ {\varepsilon }_{{\rm{N}}{\rm{i}}}^{0} $	$ 4.75\times {10}^{-4} $
	$ {\varepsilon }_{{\rm{A}}{\rm{l}}}^{0} $	$ 1.64\times {10}^{-4} $
Simulation parameters	$ {\rm{d}}x $	1	nm
	$ {\rm{d}}y $	1	nm
	$ {\rm{d}}z $	1	nm
	$ \Delta t $	0.01
$ {\kappa }_{c}, {\kappa }_{\eta } $-gradient energy coefficient; $ Y $-average stiffness; $ {V}_{{\rm{m}}} $-molar volume; $ W $-structural transformation barriers; $ {C}_{11}^{{\rm{m}}}, {C}_{12}^{{\rm{m}}}, {C}_{44}^{{\rm{m}}} $-elastic constant of the matrix phase; $ {C}_{11}^{{\rm{p}}}, {C}_{12}^{{\rm{p}}}, {C}_{44}^{{\rm{p}}} $-elastic constant of the precipitated phase; $ {\varepsilon }_{i}^{0}(i={\rm{C}}{\rm{u}}, {\rm{M}}{\rm{n}}, {\rm{N}}{\rm{i}}, {\rm{A}}{\rm{l}}) $- lattice misfit coefficients of Cu, Mn, Ni, Al; $ {\rm{d}}x, {\rm{d}}y, {\rm{d}}z $ unit length of simulated meshes; $ \Delta t $-unit time step

DownLoad: CSV

Alloy elements	Al	Cu	Mn	Ni	Fe
Al	—	–1	–19	–22	–11
Cu	–1	—	4	4	13
Mn	–19	4	—	–8	0
Ni	–22	4	–8	—	–2
Fe	–11	13	0	–2	—

DownLoad: CSV

Alloy system	t^*	$ {N}_{v} $/($ \times {10}^{23}{{\rm{m}}}^{-3}) $	f/%	r/nm	Strengthening/MPa
Al_0.4Cu_1.5Mn₁Ni₁Fe_1.5	4500	3.9291	0.0116	1.9148	1166
Al_0.5Cu_1.5Mn₁Ni₁Fe_1.5	4500	4.0817	0.0123	1.9286	1188
Al_0.6Cu_1.5Mn₁Ni₁Fe_1.5	5000	3.3951	0.0103	1.9343	1038
Al_0.7Cu_1.5Mn₁Ni₁Fe_1.5	7500	4.04	0.031	2.63	775
Whenr$\; \leqslant \;$2 nm, it is a dislocation slicing mechanism, and whenr> 2 nm, it is a dislocation bypassing mechanism.

DownLoad: CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]
[36]
[37]
[38]
[39]
[40]
[41]
[42]
[43]
[44]
[45]
[46]
[47]
[48]
[49]
[50]
[51]
[52]
[53]
[54]
[55]
[56]
[57]
[58]
[59]
[60]
[61]
[62]
[63]
[64]
[65]
[66]
[67]
[68]

[1]	Liu Zhong-Lei, Cao Jin-Ming, Wang Zhi, Zhao Yu-Hong.Phase-field method explored ferroelectric vortex topology structure and morphotropic phase boundaries. Acta Physica Sinica, 2023, 72(3): 037702.doi:10.7498/aps.72.20221898
[2]	Guo Can, Kang Chen-Rui, Gao Ying, Zhang Yi-Chi, Deng Ying-Yuan, Ma Chao, Xu Chun-Jie, Liang Shu-Hua.A phase-field model forin-situreaction process of metal-matrix composite materials. Acta Physica Sinica, 2022, 71(9): 096401.doi:10.7498/aps.71.20211737
[3]	Jiang Xin-An, Zhao Yu-Hong, Yang Wen-Kui, Tian Xiao-Lin, Hou Hua.Mechanism of internal magnetic energy of Cu-rich phase precipitation in Fe₈₄Cu₁₅Mn₁alloy by phase field method. Acta Physica Sinica, 2022, 71(8): 080201.doi:10.7498/aps.71.20212087
[4]	Huang Wen-Jun, Qiao Jun-Wei, Chen Shun-Hua, Wang Xue-Jiao, Wu Yu-Cheng.Preparation, structures and properties of tungsten-containing refractory high entropy alloys. Acta Physica Sinica, 2021, 70(10): 106201.doi:10.7498/aps.70.20201986
[5]	Yang Hui, Feng Ze-Hua, Wang He-Ran, Zhang Yun-Peng, Chen Zheng, Xin Tian-Yuan, Song Xiao-Rong, Wu Lu, Zhang Jing.Phase-field modeling of irradiated void microstructure evolution of Fe-Cr alloy. Acta Physica Sinica, 2021, 70(5): 054601.doi:10.7498/aps.70.20201457
[6]	Guo Zhen, Zhao Yu-Hong, Sun Yuan-Yang, Zhao Bao-Jun, Tian Xiao-Lin, Hou Hua.Phase field study of effect of Al on Cu-rich precipitates in Fe-Cu-Mn-Al alloys. Acta Physica Sinica, 2021, 70(8): 086401.doi:10.7498/aps.70.20201843
[7]	Wang Tao, Li Jun-Jie, Wang Jin-Cheng.Phase field modeling of the influence of interfacial wettability and solid volume fraction on the kinetics of coarsening. Acta Physica Sinica, 2013, 62(10): 106402.doi:10.7498/aps.62.106402
[8]	Wang Ya-Qin, Wang Jin-Cheng, Li Jun-Jie.Phase field modeling of the growth and competition behavior of tilted dendrites in directional solidification. Acta Physica Sinica, 2012, 61(11): 118103.doi:10.7498/aps.61.118103
[9]	Wang Ming-Guang, Zhao Yu-Hong, Ren Juan-Na, Mu Yan-Qing, Wang Wei, Yang Wei-Ming, Li Ai-Hong, Ge Hong-Hao, Hou Hua.Phase-field simulation of Non-Isothermal dendritic growth of NiCu alloy. Acta Physica Sinica, 2011, 60(4): 040507.doi:10.7498/aps.60.040507
[10]	Zong Ya-Ping, Wang Ming-Tao, Guo Wei.Phase field simulation on recrystallization and secondary phase precipitation under strain field. Acta Physica Sinica, 2009, 58(13): 161-S168.doi:10.7498/aps.58.161
[11]	Long Wen-Yuan, Lü Dong-Lan, Xia Chun, Pan Mei-Man, Cai Qi-Zhou, Chen Li-Liang.Phase-field simulation of non-isothermal solidification dendrite growth of binary alloy under the force flow. Acta Physica Sinica, 2009, 58(11): 7802-7808.doi:10.7498/aps.58.7802
[12]	Chen Yu-Juan, Chen Chang-Le.Simulation of the influence of convection velocity on upstream dendritic growth using phase-field method. Acta Physica Sinica, 2008, 57(7): 4585-4589.doi:10.7498/aps.57.4585
[13]	Feng Li, Wang Zhi-Ping, Lu Yang, Zhu Chang-Sheng.Phase-field model of isothermal solidification of binary alloy with multiple grains. Acta Physica Sinica, 2008, 57(2): 1084-1090.doi:10.7498/aps.57.1084
[14]	Li Jun-Jie, Wang Jin-Cheng, Xu Quan, Yang Gen-Cang.Effect of foreign particles on the dendritic growth in phase-field theory. Acta Physica Sinica, 2007, 56(3): 1514-1519.doi:10.7498/aps.56.1514
[15]	Long Wen-Yuan, Cai Qi-Zhou, Wei Bo-Kang, Chen Li-Liang.Simulation of dendritic growth of multicomponent alloys using phase-field method. Acta Physica Sinica, 2006, 55(3): 1341-1345.doi:10.7498/aps.55.1341
[16]	Zhang Yu-Xiang, Wang Jin-Cheng, Yang Gen-Cang, Zhou Yao-He.Phase-field simulation of the influence of elastic field on microstructure evolution and equilibrium composition of precipitation. Acta Physica Sinica, 2006, 55(5): 2433-2438.doi:10.7498/aps.55.2433
[17]	Yang Hong, Zhang Qing-Guang, Chen Min.A phase-field simulation on the influence of thermal fluctuation on secondary branch growth in undercooled melt. Acta Physica Sinica, 2005, 54(8): 3740-3744.doi:10.7498/aps.54.3740
[18]	Li Mei-E, Yang Gen-Cang, Zhou Yao-He.Phase field modeling of directional solidification of a binary alloy at high velocities. Acta Physica Sinica, 2005, 54(1): 454-459.doi:10.7498/aps.54.454
[19]	Long Wen-Yuan, Cai Qi-Zhou, Chen Li-Liang, Wei Bo-Kang.Phase-field modeling of isothermal solidification in binary alloy. Acta Physica Sinica, 2005, 54(1): 256-262.doi:10.7498/aps.54.256
[20]	Liu Hong.Surface energy of the biaxial nematic liquid crystal. Acta Physica Sinica, 2002, 51(12): 2786-2792.doi:10.7498/aps.51.2786

Catalog

Vol. 72, Issue 7 - 2023-04-05

Metrics

Abstract views:4645
PDF Downloads:111
Cited By:0

Search

Article