Snoek-type relaxation caused by interstitial atoms in sintered <i>β</i>-type Ti-Nb alloy

姓名
邮箱
手机号码
标题
留言内容
验证码

Abstract

The β-type Ti-Nb alloys are potential shape memory and superelasticity materials. The interstitial atoms in the alloys have important effect on their physical and mechanical properties. For the interstitial atoms, the internal friction technique can be used to detect their distributions and status in the alloys. The influences of chemical compositions and heat treatments on the microstructures of the containing-oxygen Ti-Nb alloys are given, and a clear understanding and the relaxational mechanism of the internal friction peak correlated with oxygen are also clearly discussed by investigating the internal friction behavior of the alloys and the detecting their microstructures. The Ti-Nb alloys with different Nb content values are prepared by powder metallurgy. The internal friction behaviors of Ti-Nb alloys with different Nb content values and heat treatments are investigated by using dynamic mechanical analysis (dynamic mechanical analyzer, DMA) Q800 from TA Instruments in single cantilever mode under different testing parameters and conditions from room temperature to 350 ℃. The X-ray diffraction experiments are also carried out in order to detect the differences among the microstructures of the specimens with different heat treatments for the Ti-35.4Nb alloy. It is shown that relaxational internal friction peaks are found on the internal friction temperature dependent curves of the sintered and water-quenched alloys. The internal friction peak is correlated with Nb content. The peak does not appear in the sintered Ti-Nb alloys with low Nb content. The maximum of the internal friction peak appears in the quenched alloy with about 35% Nb. The internal friction peak height increases monotonically with Nb content increasing in the present testing composition range for the sintered alloys. The relaxation parameters are the activation energy H_wq= (1.67 ± 0.1) eV and the preexponential factor τ _owq= 1.1 × 10 ^{－17 ± 1}s for the quenched Ti-35.4Nb alloy . In addition, the peak height also depends on heat treatment. The water-quenched Ti-35.4Nb alloy has much higher internal friction peak than the as-sintered alloy with identical compositions. The internal friction peak height is also correlated with the quenching temperature. It is found that the peak is linked to the βphase of Ti-Nb alloys and that the peak height is determined by the stability and amount of the βphase from their microstructures. When the stability of the βphase decreases, the peak height increases, and the increase in the amount of βphase results in the increase of the peak height. The βphase in the quenched Ti-35.4Nb specimen is metastable βphase ( β _M), which can be transformed into the stable αand β _Sby ageing. The βphase in as-sintered specimen is the stable βphase ( β _S). The modifications of microstructures of the specimens with different heat treatments result in the difference in peak height between the water-quenched and as-sintered Ti-35.4Nb specimens. That the peak height presents a maximum in the vicinity of 35 wt.% Nb for the quenched alloys results from the variation of the stability and amount of β _Mwith Nb content. That the height of the peak increases monotonically with Nb content increasing in as-sintered alloys is attributed to the increase of the amount of β _S. It is suggested that the internal friction peak is related to oxygen jump in lattice or the interaction between the oxygen-substitute atoms in β _Mphase for the water-quenched alloys and those in β _Sphase for the as-sintered alloys.

Keywords:

Authors and contacts

Corresponding author:Zhou Zheng-Cun,1355326160@qq.com

FullText HTML: translate this paragraph

References

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]

Cited By

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

DownLoad: Full-Size Img PowerPoint

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]

[1]	Mi Xiao-Lei, Hu Liang, Wu Bo-Wen, Long Qiang, Wei Bing-Bo.Influence of gadolinium content on magnetic property and oxidation mechanism of Fe-B-Nb-Gd metallic glass. Acta Physica Sinica, 2024, 73(9): 097102.doi:10.7498/aps.73.20232040
[2]	Li Yu-Chuan, Hao Gang-Ling, Wang Jin, Wang Wei-Guo, Wang Xin-Fu, Wang Dan.Internal friction of Ni-Al intermetallic compound formation in sintering process. Acta Physica Sinica, 2021, 70(5): 056102.doi:10.7498/aps.70.20201422
[3]	Lu Xiao-Mei, Huang Feng-Zhen, Zhu Jin-Song.Domains in ferroelectrics: formation, structure, mobility and related properties. Acta Physica Sinica, 2020, 69(12): 127704.doi:10.7498/aps.69.20200312
[4]	Hao Gang-Ling, Xu Qiao-Ping, Li Xian-Yu, Wang Wei-Guo.Internal friction characteristics of compacted billet of metal powder in sintering process. Acta Physica Sinica, 2019, 68(12): 126101.doi:10.7498/aps.68.20190031
[5]	Cheng Chao, Wang Xun, Sun Jia-Xing, Cao Chao-Ming, Ma Yun-Li, Liu Yan-Xia.Electronic structure calculation of Cr content effect on corrosion resistance of Ti-Nb-Cr alloy. Acta Physica Sinica, 2018, 67(19): 197101.doi:10.7498/aps.67.20180956
[6]	Yang Jing-Jie, Zhao Jin-Liang, Xu Lei, Zhang Hong-Guo, Yue Ming, Liu Dan-Min, Jiang Yi-Jian.Influences of interstitial atoms H, B and C on magnetic properties and magnetocaloric effect in LaFe11.5Al1.5 compound. Acta Physica Sinica, 2018, 67(7): 077501.doi:10.7498/aps.67.20172250
[7]	Huang Ao, Lu Zhi-Peng, Zhou Meng, Zhou Xiao-Yun, Tao Ying-Qi, Sun Peng, Zhang Jun-Tao, Zhang Ting-Bo.Effects of the doping of Al and O interstitial atoms on thermodynamic properties of -Al2O3:first-principles calculations. Acta Physica Sinica, 2017, 66(1): 016103.doi:10.7498/aps.66.016103
[8]	Jiang Wen-Quan, Du Guang-Yu, Ba De-Chun, Yang Fan.Micro-mechanism of damping vibration attenuation on porous metal coating. Acta Physica Sinica, 2015, 64(14): 146801.doi:10.7498/aps.64.146801
[9]	Rao Jian-Ping, Ouyang Chu-Ying, Lei Min-Sheng, Jiang Feng-Yi.First principles investigation of interaction between interstitials H atom and Nb metal. Acta Physica Sinica, 2012, 61(4): 047105.doi:10.7498/aps.61.047105
[10]	Wu Xiao-Yi, Xiong Xiao-Min, Zhang Jin-Xiu.Torsion strain spectrum and its application to in phase transformation. Acta Physica Sinica, 2012, 61(1): 014601.doi:10.7498/aps.61.014601
[11]	Wu Xiu-Sheng, Yang Chun-Li, Chen Zhi-Jun, Chen Chu-Sheng, Liu Wei.Low-frequency internal friction study of La1-xSrxFeO3-δ（0≤x≤2/3）system. Acta Physica Sinica, 2009, 58(9): 6419-6424.doi:10.7498/aps.58.6419
[12]	Sun Wei, Wang Qing-Zhou, Han Fu-Sheng.The internal friction related to dislocation peak in a graphite particulate CuAlMn shape memory alloy composite. Acta Physica Sinica, 2007, 56(2): 1020-1026.doi:10.7498/aps.56.1020
[13]	Peng Kai-Ping, Chen Wen-Zhe, Qian Kuang-Wu.Study of an anomalous serrated yielding phenomenon in 3004 aluminum alloy. Acta Physica Sinica, 2006, 55(7): 3569-3575.doi:10.7498/aps.55.3569
[14]	Zhang Hua-Li, Liu Wei, Li Dong-Cai, Wu Xiu-Sheng, Chen Chu-Sheng.Phase separation in La2NiO4+δ studied by lowfrequency internal friction technique. Acta Physica Sinica, 2004, 53(11): 3834-3838.doi:10.7498/aps.53.3834
[15]	Wang Qiang, Zhou Zheng-Cun, Han Fu-Sheng.The two internal friction peaks in rapidly cooled Fe71Al29 alloy*. Acta Physica Sinica, 2004, 53(11): 3829-3833.doi:10.7498/aps.53.3829
[16]	Guo Li-Jun, Zhu Fang-Qiu, Zhu Zhen-Gang.. Acta Physica Sinica, 2002, 51(2): 300-303.doi:10.7498/aps.51.300
[17]	LIANG YUN-FENG, SHUI JIA-PENG, CHEN GANG, ZHU ZHEN-GANG.INTERNAL FRICTION BEHAVIOUR OF THE SOLID－LIQUID TRANSITION IN THE Pb-Sn ALLOYS. Acta Physica Sinica, 2000, 49(7): 1327-1330.doi:10.7498/aps.49.1327
[18]	.关于面心立方体金属中间隙原子内耗理论一文的更正. Acta Physica Sinica, 1961, 17(11): 53-54.doi:10.7498/aps.17.53
[19]	.关于面心立方体合金中间隙原子内耗机构的探讨. Acta Physica Sinica, 1961, 17(11): 555-558.doi:10.7498/aps.17.555
[20]	CHENG KAI-CHIA, CHANG SHEN-KWAI.THEORY OF INTERNAL FRICTION IN A FACE-CENTRED CUBIC LATTICE. Acta Physica Sinica, 1958, 14(1): 71-81.doi:10.7498/aps.14.71

Catalog

Vol. 68, Issue 8 - 2019-04-20

Metrics

Abstract views:5947
PDF Downloads:42
Cited By:0

Search

Article