摘要

先进铅冷快堆和加速器驱动次临界系统商业化的关键材料问题是结构材料与铅基冷却剂之间的相容性问题, 结构钢材料需要在高温液态铅铋共晶中具有优异的抗腐蚀能力. 含铝强化奥氏体钢(alumina-forming austenite steel, AFA钢)因其表面可以形成Al ₂O ₃膜而在极端环境中具有良好的耐蚀性能. 本文研究了降低Ni元素成分和高温预氧化对AFA钢耐铅铋腐蚀性能的影响, 利用扫描电子显微镜、能量色散X射线光谱仪、X射线衍射技术, 对AFA钢在550 ℃液态铅铋饱和溶氧条件下腐蚀600 h的氧化层形貌及结构进行表征. 结果表明: 降低合金中Ni含量和高温预氧化处理都会促进样品表面形成保护性Al ₂O ₃氧化膜, 进而降低腐蚀层厚度, 提升材料耐铅铋腐蚀性能.

关键词:

Abstract

The key material issue for the commercialization of advanced lead cooled fast reactors and accelerator driven subcritical systems is the compatibility between structural materials and lead based coolants. Structural steel materials require excellent corrosion resistance in high-temperature liquid lead bismuth eutectic (LBE) alloy. Aluminum forming austenitic steel (AFA steel) has excellent corrosion resistance in extreme environments due to its ability to form an Al ₂O ₃film on its surface. However, excessively high Ni elements are more easily dissolved or oxidized in LBE than Fe and Cr elements. Therefore, this work investigates the effect of reducing Ni element composition (25-Ni steel and 18-Ni steel) on the corrosion resistance of steel in LBE. Surface treatment can protect the substrate from corrosion to some extent, so herein we explore whether it has a protective effect on AFA steel in LBE by generating Al ₂O ₃through high-temperature pre oxidation. The morphology and structure of the oxide layer of AFA steel corroded for 600 h in LBE with saturated dissolved oxygen at 550 ℃ are characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD), and other technologies. The results indicate that the oxide film formed after corrosion of 18-Ni steel is thinner than that after corrosion of 25-Ni steel. Performing high-temperature pre oxidation is beneficial to forming a protective Al ₂O ₃oxide film on the surface of the sample, thereby reducing the thickness of the oxide layer and improving the material’s LBE corrosion resistance. The reduction in thickness of the oxide layer generated after pre oxidation of 18-Ni steel is greater than that of 25-Ni steel, so the anti-corrosion effect of 18-Ni steel after pre oxidation is better than that of 25-Ni steel.

Keywords:

作者及机构信息

1.
2.
3.

通信作者:徐帅,shuaixu2020@swust.edu.cn

基金项目:高等学校博士学科点专项科研基金 (批准号: 20zx7104)资助的课题.

Authors and contacts

1.
2.
3.

Corresponding author:Xu Shuai,shuaixu2020@swust.edu.cn

Funds:Project supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20zx7104).

文章全文: translate this paragraph

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]
[36]
[37]
[38]
[39]
[40]
[41]
[42]
[43]
[44]
[45]
[46]
[47]
[48]
[49]
[50]

施引文献

下载: 全尺寸图片幻灯片

	Ni	Cr	Al	Mo	Nb	Fe
18-Ni	19.25	14.21	2.66	3.62	1.8	Bal.
25-Ni	26.67	14.11	2.76	3.55	1.81	Bal.

下载: 导出CSV

区域	Cr	Al	Fe	Nb	O
点1	0.3	0	43.3	2.7	53.6
点2	2.2	13.6	10.6	12.4	47.0
点3	1.9	16.6	7.3	2.0	48.2
点4	1.3	0.5	58.9	0.7	35.5
点5	18.8	1.9	36.4	2.2	37.0
点6	8.6	8.6	34.0	17.5	7.9

下载: 导出CSV

区域	Cr	Al	Fe	O
点7	3.28	1.51	50.12	38.59
点8	9.94	14.24	44.26	9.46
点9	7.56	2.18	51.11	36.15
点10	25.00	5.88	38.62	22.34
点11	15.42	0.69	75.67	5.20

下载: 导出CSV

区域	Cr	Al	Fe	Ni	O
点12	9.2	4.4	49.5	4.2	30.9
点13	1.5	39.7	2.6	2.1	53.5
点14	1.1	1.1	85.7	0.0	10.9
点15	2.1	17.8	7.4	20.9	5.20

下载: 导出CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]
[36]
[37]
[38]
[39]
[40]
[41]
[42]
[43]
[44]
[45]
[46]
[47]
[48]
[49]
[50]

[1]	况丹, 徐爽, 史大为, 郭建, 喻志农.基于铝纳米颗粒修饰的非晶氧化镓薄膜日盲紫外探测器. 必威体育下载 , 2023, 72(3): 038501.doi:10.7498/aps.72.20221476
[2]	廖庆, 李炳生, 葛芳芳, 张宏鹏, 申铁龙, 毛雪丽, 王任大, 盛彦斌, 常海龙, 王志光, 徐帅, 陈黎明, 何晓珣.T91钢和SIMP钢表面AlO_x涂层在600 ℃静态液态铅铋共晶中的稳定性和腐蚀行为. 必威体育下载 , 2022, 71(15): 156103.doi:10.7498/aps.71.20220356
[3]	陈东运, 高明, 李拥华, 徐飞, 赵磊, 马忠权.MoO₃/Si界面区钼掺杂非晶氧化硅层形成的第一性原理研究. 必威体育下载 , 2019, 68(10): 103101.doi:10.7498/aps.68.20190067
[4]	丁翠, 刘充, 张庆华, 龚冠铭, 汪恒, 刘效治, 孟繁琦, 杨好好, 武睿, 宋灿立, 李渭, 何珂, 马旭村, 谷林, 王立莉, 薛其坤.单层FeSe薄膜/氧化物界面高温超导. 必威体育下载 , 2018, 67(20): 207415.doi:10.7498/aps.67.20181681
[5]	高娅娜, 李喜峰, 张建华.溶胶凝胶法制备高性能锆铝氧化物作为绝缘层的薄膜晶体管. 必威体育下载 , 2014, 63(11): 118502.doi:10.7498/aps.63.118502
[6]	王平, 郭立新, 杨银堂, 张志勇.铝氮共掺杂氧化锌纳米管电子结构的第一性原理研究. 必威体育下载 , 2013, 62(5): 056105.doi:10.7498/aps.62.056105
[7]	刘贵立, 李勇.钛铝合金高温氧化机理电子理论研究. 必威体育下载 , 2012, 61(17): 177101.doi:10.7498/aps.61.177101
[8]	张国英, 李丹, 梁婷.铌合金电子结构及其高温氧化行为. 必威体育下载 , 2010, 59(11): 8031-8036.doi:10.7498/aps.59.8031
[9]	刘贵立.Nb-Al合金高温氧化机理. 必威体育下载 , 2010, 59(1): 499-503.doi:10.7498/aps.59.499
[10]	李蕾蕾, 刘红侠, 于宗光, 郝跃.恒流应力下E2PROM隧道氧化层的退化特性研究. 必威体育下载 , 2006, 55(5): 2459-2463.doi:10.7498/aps.55.2459
[11]	马晓华, 郝跃, 陈海峰, 曹艳荣, 周鹏举.电压应力下超薄栅氧化层n-MOSFET的击穿特性. 必威体育下载 , 2006, 55(11): 6118-6122.doi:10.7498/aps.55.6118
[12]	靳惠明, Felix Adriana, Aroyave Majorri.离子注钇对镍900℃高温氧化行为及氧化膜性能的影响研究. 必威体育下载 , 2006, 55(11): 6157-6162.doi:10.7498/aps.55.6157
[13]	冯玉清, 侯利娜, 朱涛, 姚淑德, 詹文山.具有纳米氧化层的磁性隧道结的热稳定性研究. 必威体育下载 , 2005, 54(9): 4340-4344.doi:10.7498/aps.54.4340
[14]	马仲发, 庄奕琪, 杜磊, 包军林, 李伟华.栅氧化层介质经时击穿的逾渗模型. 必威体育下载 , 2003, 52(8): 2046-2051.doi:10.7498/aps.52.2046
[15]	刘红侠, 郑雪峰, 郝跃.薄栅氧化层中陷阱电荷密度的测量方法. 必威体育下载 , 2002, 51(1): 163-166.doi:10.7498/aps.51.163
[16]	刘红侠, 郝跃.应力导致的薄栅氧化层漏电流瞬态特性研究. 必威体育下载 , 2001, 50(9): 1769-1773.doi:10.7498/aps.50.1769
[17]	严辉, 马黎君, 陈光华, 黄世平, 文华杰, 郭伟明.金属Sn薄膜的高温氧化与表面特征. 必威体育下载 , 1997, 46(8): 1658-1664.doi:10.7498/aps.46.1658
[18]	吴坚, 陆怀先, 都有为, 高学奎, 王挺祥.超细Fe微粒表面氧化层的磁性研究. 必威体育下载 , 1988, 37(12): 2044-2047.doi:10.7498/aps.37.2044
[19]	李克诚, 薛士蓥, 祝忠德, 黄詠.磷在硅表面氧化层中的扩散. 必威体育下载 , 1965, 21(3): 496-502.doi:10.7498/aps.21.496
[20]	.利用谱线宽度法作钢中渗铝层逐层分析试验报告. 必威体育下载 , 1959, 15(6): 305-310.doi:10.7498/aps.15.305

计量

文章访问数:1489
PDF下载量:41
被引次数:0

搜索

留言板