实验研究了复合添加微量元素La和Al-5Ti-1B对Al-Cu合金凝固组织的影响, 发现与单独添加Al-5Ti-1B相比, 复合添加Al-5Ti-1B和微量La可进一步细化Al-Cu合金凝固组织, 降低 α-Al的形核过冷度. 结合高分辨透射电镜表征和理论计算, 探明了复合添加微量元素La和Al-5Ti-1B对Al-Cu合金凝固组织的细化机理: 经Al-5Ti-1B细化处理的Al-Cu合金凝固时, Cu富集于 α-Al与TiB ₂粒子的界面处, 增加了 α-Al与TiB ₂粒子间的错配度, 降低了TiB ₂粒子对 α-Al的异质形核能力; 添加微量的La能有效降低 α-Al与TiB ₂粒子间的错配度, 减小TiB ₂粒子和 α-Al间的界面能及接触角, 从而提高TiB ₂粒子促进 α-Al的异质形核能力和Al-5Ti-1B对Al-Cu合金晶粒的细化效果.

关键词:

Abstract

Grain refinement of aluminium alloys can not only reduce the defects (such as segregation and hot tearing) but also improve the mechanical properties. Adding Al-5Ti-1B master alloy to the melt has become a common method to refine the solidification microstructure of aluminium alloys. A lot of researches have been carried out to uncover the grain refining mechanisms as well as to show the microstructure formation under the effect of grain refiner. These researches demonstrated that the grain refining efficiency is closely related to the number density of TiB ₂particles as well as the solute Ti concentration in the melt. However, there exist still problems to be resolved, such as the limited grain refinement potency of Al-5Ti-1B master alloy. Recently, the addition of trace La to the melt has attracted much attention to control the microstructure of aluminium alloys. The Al-Cu alloys are widely applied to the automobile and aerospace fields due to their high strength, good ductility and high temperature properties. It has been reported that Cu can segregate to Al/TiB ₂interface in the Al-Cu melt inoculated with Al-5Ti-1B master alloy. But the effect of Cu segregation on the grain refinement result is not clear yet. Meanwhile, whether the grain refinement effect of Al-5Ti-1B master alloy on Al-Cu alloy can be improved by the addition of trace La has not been reported. Solidification experiments are carried out for Al-2Cu alloy with the addition of Al-5Ti-1B master alloy+ trace La. The synergistic effect of trace La and Al-5Ti-1B on the solidification microstructure of Al-2Cu alloy is investigated. It is found that trace La can effectively enhance the refinement result of Al-2Cu alloy and further diminish the nucleation undercooling. Experimental and calculated results demonstrate that solute Cu segregates to the Al/TiB ₂interface and thus increases the interatomic spacing mismatch between Ti (0001) plane of the TiB ₂particles and the interfacial monolayer, while La segregation reduces the interatomic spacing mismatch. The trace La addition reduces the interfacial energy between α-Al and TiB ₂particles, improves the potency of TiB ₂particles to nucleate α-Al, and thus enhances the grain refinement result of Al-5Ti-1B master alloy.

Keywords:

作者及机构信息

1.
2.

通信作者:张丽丽,llzhang@imr.ac.cn; 赵九洲,jzzhao@imr.ac.cn

基金项目:国家重点研发计划(批准号: 2021YFA0716303)、中国载人航天工程和国家自然科学基金(批准号: 51901231, 51971227)资助的课题.

Authors and contacts

1.
2.

Corresponding author:Zhang Li-Li,llzhang@imr.ac.cn; Zhao Jiu-Zhou,jzzhao@imr.ac.cn

Funds:Project supported by the National Key R&D Program of China (Grant No. 2021YFA0716303), the China Manned Space Station Project, and the National Natural Science Foundation of China (Grant Nos. 51901231, 51971227).

文章全文: translate this paragraph

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]

施引文献

下载: 全尺寸图片幻灯片

i	k_i	m_i/(K·%^–1)	$ {c'_{{\text{S}}i}}/\% $	$ {c'_{{\text{L}}i}}/\% $	Reference
Ti	7.8	33.3	—	—	[12]
Cu	0.17	–3.4	5.69	32.5	[34]
La	0.004	–1.71	0.05	11.7	[35]

下载: 导出CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]
[32]
[33]
[34]
[35]

[1]	戴宇佳, 李明亮, 宋超, 高勋, 郝作强, 林景全.空间约束结合梯度下降法提高铝合金中Fe成分激光诱导击穿光谱技术检测精度. 必威体育下载 , 2021, 70(20): 205204.doi:10.7498/aps.70.20210792
[2]	宋岩, 江鸿翔, 赵九洲, 何杰, 张丽丽, 李世欣.Al-Ti-B细化工业纯铝凝固组织演变过程数值模拟. 必威体育下载 , 2021, 70(8): 086402.doi:10.7498/aps.70.20201431
[3]	郭志超, 李平林.晶粒细化对MgB2超导临界电流密度的作用. 必威体育下载 , 2014, 63(6): 067401.doi:10.7498/aps.63.067401
[4]	管仁国, 赵占勇, 黄红乾, 连超, 钞润泽, 刘春明.冷却倾斜板熔体处理过程边界层分布及流动传热的理论研究. 必威体育下载 , 2012, 61(20): 206602.doi:10.7498/aps.61.206602
[5]	张辉, 吴迪, 张国英, 肖明珠.铜基大块非晶合金添加微量元素对腐蚀行为的影响机理研究. 必威体育下载 , 2010, 59(1): 488-493.doi:10.7498/aps.59.488
[6]	孙对兄, 苏茂根, 董晨钟, 王向丽, 张大成, 马新文.基于激光诱导击穿光谱技术的铝合金成分定量分析. 必威体育下载 , 2010, 59(7): 4571-4576.doi:10.7498/aps.59.4571
[7]	王娜, 唐壁玉.L12型铝合金的结构、弹性和电子性质的第一性原理研究. 必威体育下载 , 2009, 58(13): 230-S234.doi:10.7498/aps.58.230
[8]	樊飞, 班春燕, 王洋, 巴启先, 崔建忠.普通铸造和低频电磁铸造7050铝合金电阻率-温度特性的研究. 必威体育下载 , 2009, 58(1): 638-643.doi:10.7498/aps.58.638
[9]	刘贵立.Mg合金晶粒细化机理的电子理论研究. 必威体育下载 , 2009, 58(5): 3319-3323.doi:10.7498/aps.58.3319
[10]	刘贵立.Mg-Zr合金微观组织电子结构研究. 必威体育下载 , 2008, 57(2): 1043-1047.doi:10.7498/aps.57.1043
[11]	张大成, 马新文, 朱小龙, 李斌, 祖凯玲.激光诱导击穿光谱应用于三种水果样品微量元素的分析. 必威体育下载 , 2008, 57(10): 6348-6353.doi:10.7498/aps.57.6348
[12]	郑里平, 李斗星, 许子健, 朱志远.用双粒子模型研究微量元素与Ni在Ni3Al晶界共富集现象. 必威体育下载 , 2007, 56(3): 1520-1525.doi:10.7498/aps.56.1520
[13]	张国英, 张辉, 刘春明, 周永军.微合金化元素晶界偏聚与钢的超细化理论研究. 必威体育下载 , 2006, 55(3): 1369-1373.doi:10.7498/aps.55.1369
[14]	庞雪君, 王强, 王春江, 王亚勤, 李亚彬, 赫冀成.强磁场对铝合金中溶质组元分布状态的影响效果. 必威体育下载 , 2006, 55(10): 5129-5134.doi:10.7498/aps.55.5129
[15]	彭开萍, 陈文哲, 钱匡武.3004铝合金“反常”锯齿屈服现象的研究. 必威体育下载 , 2006, 55(7): 3569-3575.doi:10.7498/aps.55.3569
[16]	吴汉华, 龙北红, 吕宪义, 汪剑波, 金曾孙.铝合金微弧氧化过程中电学参量的特性研究. 必威体育下载 , 2005, 54(4): 1697-1701.doi:10.7498/aps.54.1697
[17]	张国英, 张辉, 刘春明, 周永军.钢铁材料中形变诱导相变超细化机理研究. 必威体育下载 , 2005, 54(4): 1771-1776.doi:10.7498/aps.54.1771
[18]	朱波, 蔡珣, 王成国, 蔡华甦.声发射特性与材料断裂韧性相关性研究. 必威体育下载 , 2003, 52(8): 1960-1964.doi:10.7498/aps.52.1960
[19]	张勤, 班春燕, 崔建忠, 巴启先, 路贵民, 张北江.ＣＲＥＭ法半连铸Ａｌ合金过程中电磁场对溶质元素固溶的影响机理. 必威体育下载 , 2003, 52(10): 2642-2648.doi:10.7498/aps.52.2642
[20]	王震遐, 潘冀生, 章骥平, 陶振兰.合金在离子择优溅射中的表面元素局域富集效应. 必威体育下载 , 1992, 41(10): 1722-1727.doi:10.7498/aps.41.1722

计量

文章访问数:2811
PDF下载量:47
被引次数:0

搜索

留言板