摘要

碲锌镉探测器长期暴露于辐射环境下时, 会形成不同程度的辐照损伤, 影响器件性能甚至失效, 极大缩短探测器在辐射场中的服役时限. 本文首先利用Geant4程序包对能量为1.00—14.00 MeV的中子在碲锌镉中的输运过程进行模拟, 获取初级离位原子的信息, 进而结合级联碰撞模型, 对不同能量的中子在碲锌镉材料中造成的辐照损伤进行模拟计算. 计算结果表明初级离位原子能量大部分位于低能端, 并随着入射中子能量升高, 初级离位原子的种类更加丰富, 能量也逐渐增大; 中子辐照碲锌镉材料时非电离能损沿着深度方向均匀分布, 且非电离能损随着入射中子能量的增加呈现先增大后减小的趋势; 辐照损伤量—原子离位次数(dpa)的计算结果表明, dpa也随入射中子能量升高呈先增大后减小的趋势, 进一步分析可知随着入射中子能量增大, 非弹性散射成为造成材料内部离位损伤的主要因素.

关键词:

Abstract

In recent years, the development of new semiconductor materials has made an opportunity and challenge for technological innovation and the development of emerging industries. Among them, cadmium zinc telluride materials have highlighted important application prospects due to their excellent properties. The CdZnTe, as the third-generation cutting-edge strategic semiconductor material, has the advantages of high detection efficiency, low dark current, strong portability, and applicability at room temperature without additional cooling system. However, when the cadmium zinc telluride detector is exposed to radiation environment for a long time, it will cause different degrees of radiation damage, which will affect the performance of the device or even fail to work, and greatly shorten the service time of the detector in the radiation field. The transport process of 1.00–14.00 MeV neutrons in CdZnTe material is simulated to obtain the information about the primary knock-on atoms, and then by combining with the cascade collision model, the irradiation of neutrons with different energy in CdZnTe material is analyzed. The damage is simulated and calculated. The calculation results are shown below. The energy of most of the primary knock-on atoms is located at the low-energy end, and with the increase of the incident neutron energy, the types of primary knock-on atoms are more abundant, and the energy also increases gradually. With neutron irradiation of CdZnTe, the non-ionizing energy loss is uniformly distributed along the depth direction in the material, and the non-ionizing energy loss first increases and then decreases with the increase of the incident neutron energy. The calculation results of displacements per atom(dpa) show that the dpa also increases first with the increase of the incident neutron energy. And further analysis shows that the number of Te displacement atom atoms and the number of the Zn displacement atoms both increase first and decrease then with the increase of incident neutron energy, while the number of Cd displacement atoms increases with the increase of incident neutron energy, which is co-modulated by its inelastic scattering cross-section and other nuclear-like reaction cross-sections. The comprehensive analysis shows that with the increase of the incident neutron energy, inelastic scattering becomes the main factor causing the internal displacement damage of the material.

Keywords:

作者及机构信息

通信作者:李公平,ligp@lzu.edu.cn

基金项目:国家自然科学基金(批准号: 11975006, 11575074)和兰州大学特殊功能材料与结构设计教育部重点实验室(B类)2021年开放课题(批准号: lzujbky-2021-kb06)资助的课题.

Authors and contacts

Corresponding author:Li Gong-Ping,ligp@lzu.edu.cn

Funds:Project supported by the National Natural Science Foundation of China (Grant Nos. 11975006, 11575074), and the Open Project of Key Laboratory of Special Functional Materials and Structural Design of the Ministry of Education (Class B) of Lanzhou University in 2021 (Grant No. lzujbky-2021-kb06).

文章全文: translate this paragraph

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]

施引文献

下载: 全尺寸图片幻灯片

Energy/ MeV	Element	Recoil atoms	E_k	E_dam(T)	Percentage/%
2.45	Cd	¹¹⁴Cd(12.57%)¹¹²Cd(10.47%)¹¹¹Cd(5.57%)¹¹³Cd(5.44%) ¹¹⁰Cd(5.33%)¹¹⁶Cd(3.31%)^{106—109, 115, 117}Cd(0.98%)	0.002 eV— 91.79 keV	0.002 eV— 76.80 keV	43.67
	Te	¹³⁰Te(18.43%)¹²⁸Te(16.58%)¹²⁶Te(9.94%)¹²⁵Te(3.71%)¹²⁴Te(2.51%) ¹²²Te(1.32%)^{120, 121, 123, 127, 129, 131}Te(0.58%)	0.03 eV— 81.05 keV	0.03 eV— 69.68 keV	53.05
	Zn	⁶⁴Zn(1.59%)⁶⁶Zn(0.93%)⁶⁸Zn(0.55%)^{65, 67, 69—70}Zn(0.15%)	1.33 eV— 150.18 keV	1.29 eV— 102.91 keV	3.23
	Other	¹H⁴He^{61, 64}Ni⁶⁴Cu etc.	527.59 eV— 5.62 MeV	492.12 eV— 239.7 keV	0.05
14.00	Cd	¹¹²Cd(11.47%)¹¹⁴Cd(10.38%)¹¹³Cd(9.46%)¹¹¹Cd(8.68%)¹¹⁰Cd(7.08%) ¹¹⁶Cd(2.66%)¹⁰⁹Cd(2.02%)¹¹⁵Cd(1.47%)^{105—108, 117}Cd(1.12%)	0.07 eV— 548.26 keV	0.07 eV— 314.20 keV	54.34
	Te	¹³⁰Te(13.88%)¹²⁸Te(13.17%)¹²⁶Te(7.87%)¹²⁵Te(2.85%)¹²⁴Te(2.02%) ¹²²Te(1.10%)^{120—121, 123, 127, 129, 131}Te(0.41%)	0.05 eV— 458.06 keV	0.05 eV— 279.67 keV	41.29
	Zn	⁶⁴Zn(1.30%)⁶⁶Zn(0.87%)⁶⁸Zn(0.54%)^{65, 67, 69—70}Zn(0.13%)	0.87 eV— 861.92 keV	0.85 eV— 325.25 keV	2.83
	H	¹H(0.71%)²H(0.02%)	2.17 keV— 14.60 MeV	313.33 eV— 1.69 keV	0.73
	Other	⁴He(0.26%)^{61, 63—65, 67}Ni^{63—68, 70}Cu^{120—128, 130}Sb^{102—111, 113}Pd ^{105—114, 116}Ag^{117, 119—123, 125, 127}Sn etc.	328.98 eV— 19.94 MeV	315.24 eV— 0.66 MeV	0.81

下载: 导出CSV

Energy/ MeV	Element	Recoil atoms	E_k	E_dam(T)	Percen- tage
1.00	Cd	¹¹⁴Cd (13.61%),¹¹²Cd (11.30%),¹¹¹Cd (6.00%) ¹¹³Cd(5.83%),¹¹⁰Cd (5.80%),¹¹⁶Cd (3.56%) ^{106—109, 115, 117}Cd (1.06%)	0.03 eV—37.49 keV	0.03 eV—32.95 keV	47.16%
	Te	¹³⁰Te (16.79%),¹²⁸Te(15.86%),¹²⁶Te (9.30%)¹²⁵Te (3.51%), ¹²⁴Te (2.40%),¹²²Te (1.27%)^{120, 121, 123, 127, 129, 131}Te (0.57%)	0.02 eV—33.17 keV	0.02 eV—29.67 keV	49.69%
	Zn	⁶⁴Zn (1.55%),⁶⁶Zn (0.87%),⁶⁸Zn (0.57%) ^{65, 67, 69—71}Zn (0.15%)	0.10 eV—61.31 keV	0.10 eV—47.55 keV	3.14%
	Other	⁴He,⁶¹Ni, etc.	0.12—3.84 MeV	5.88—171.64 keV	0.01%
2.45	Cd	¹¹⁴Cd(12.57%),¹¹²Cd(10.47%),¹¹¹Cd(5.57%)¹¹³Cd(5.44%), ¹¹⁰Cd(5.33%),¹¹⁶Cd(3.31%)^{106—109, 115, 117}Cd(0.98%)	0.002 eV—91.79 keV	0.002 eV—76.80 keV	43.67%
	Te	¹³⁰Te(18.43%),¹²⁸Te(16.58%),¹²⁶Te(9.94%)¹²⁵Te(3.71%), ¹²⁴Te(2.51%),¹²²Te(1.32%)^{120, 121, 123, 127, 129, 131}Te(0.58%)	0.03 eV—81.05 keV	0.03 eV—69.68 keV	53.05%
	Zn	⁶⁴Zn(1.59%),⁶⁶Zn(0.93%),⁶⁸Zn(0.55%)^{65, 67, 69—70}Zn(0.15%)	1.33 eV—150.18 keV	1.29 eV—102.91 keV	3.23%
	Other	¹H,⁴He,^{61, 64}Ni,⁶⁴Cu, etc.	527.59 eV—5.62 MeV	492.12 eV—239.77 keV	0.05%
5.00	Cd	¹¹⁴Cd(12.56%),¹¹²Cd(10.53%),¹¹¹Cd(5.60%)¹¹⁰Cd(5.39%), ¹¹³Cd(5.32%),¹¹⁶Cd(3.33%)^{106—109, 115, 117}Cd(0.93%)	0.04 eV—187.28 keV	0.04 eV—147.18 keV	43.66%
	Te	¹³⁰Te(17.82%),¹²⁸Te(16.26%),¹²⁶Te(9.67%)¹²⁵Te(3.61%), ¹²⁴Te(2.45%),¹²²Te(1.30%)^{120, 121, 123, 127, 129, 131}Te(0.54%)	0.02 eV—163.22 keV	0.02 eV—133.96 keV	51.65%
	Zn	⁶⁴Zn(2.07%),⁶⁶Zn(1.26%),⁶⁸Zn(0.86%)^{65, 67, 69—71}Zn(0.21%)	0.20 eV—306.43 keV	0.20 eV—150.03 keV	4.39%
	Other	^{64, 66—67}Cu,^{103, 108}Pd,¹H,⁴He^{61, 63—65}Ni,^{106, 108}Ag, etc.	163.93 eV—10.68 MeV	154.95 eV—368.6 keV	0.30%
10.00	Cd	¹¹⁴Cd(13.72%),¹¹²Cd(13.72%),¹¹⁰Cd(7.19%)¹¹¹Cd(5.30%), ¹¹³Cd(4.80%),¹¹⁶Cd(3.44%)^{106—109, 115, 117}Cd(1.32%)	0.04 eV—387.48 keV	0.04 eV—234.63 keV	49.08%
	Te	¹³⁰Te(15.10%),¹²⁸Te(15.02%),¹²⁶Te(9.37%)¹²⁵Te(2.65%), ¹²⁴Te(2.50%),¹²²Te(1.37%)^{120, 123, 127, 129, 131}Te(0.42%)	0.02 eV—327.02 keV	0.02 eV—207.62 keV	46.42%
	Zn	⁶⁴Zn(1.77%),⁶⁶Zn(1.15%),⁶⁸Zn(0.81%)^{67, 69—70}Zn(0.17%)	0.21 eV—614.56 keV	0.21 eV—256.14 keV	3.90%
	Other	^1—2H(0.21%),^{63—64, 66—68}Cu(0.17%),⁴He (0.10%)^{61, 63—65}Ni, ^{102—103, 105, 107—108, 110}Pd^{117, 119—123, 127}Sn,^{106, 108, 110—114}Ag ^{120, 122—126, 128, 130}Sb, etc.	1940.87 eV—15.72 MeV	554.83 eV—547.11 keV	0.60%
14.00	Cd	¹¹²Cd(11.47%),¹¹⁴Cd(10.38%),¹¹³Cd(9.46%)¹¹¹Cd(8.68%), ¹¹⁰Cd(7.08%),¹¹⁶Cd(2.66%)¹⁰⁹Cd(2.02%),¹¹⁵Cd(1.47%) , ^{105—108, 117}Cd(1.12%)	0.07 eV—548.26 keV	0.07 eV—314.20 keV	54.34%
	Te	¹³⁰Te(13.88%),¹²⁸Te(13.17%),¹²⁶Te(7.87%)¹²⁵Te(2.85%), ¹²⁴Te(2.02%),¹²²Te(1.10%)^{120—121, 123, 127, 129, 131}Te(0.41%)	0.05 eV—458.06 keV	0.05 eV—279.67 keV	41.29%
	Zn	⁶⁴Zn(1.30%),⁶⁶Zn(0.87%),⁶⁸Zn(0.54%)^{65, 67, 69—70}Zn(0.13%)	0.87 eV—861.92 keV	0.85 eV—325.25 keV	2.83%
	H	¹H(0.71%),²H(0.02%)	2.17 keV—14.60 MeV	313.33 eV—1.69 keV	0.73%
	Other	⁴He (0.26%),^{61, 63—65, 67}Ni,^{63—68, 70}Cu^{120—128, 130}Sb, ^{102—111, 113}Pd,^{105—114, 116}Ag^{117, 119—123, 125, 127}Sn, etc.	328.98 eV—19.94 MeV	315.24 eV—0.66 MeV	0.81%

下载: 导出CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]
[21]
[22]
[23]
[24]
[25]
[26]
[27]
[28]
[29]
[30]
[31]

[1]	赵珀, 王建强, 陈梅清, 杨金学, 苏钲雄, 卢晨阳, 刘华军, 洪智勇, 高瑞.EuBa₂Cu₃O_7–δ超导带材中掺杂相对He⁺离子辐照缺陷演化及超导电性的影响. 必威体育下载 , 2024, 73(8): 087401.doi:10.7498/aps.73.20240124
[2]	曹嵩, 殷雯, 周斌, 胡志良, 沈飞, 易天成, 王松林, 梁天骄.中国散裂中子源二期靶站关键部件辐照损伤模拟计算. 必威体育下载 , 2024, 73(9): 092501.doi:10.7498/aps.73.20240088
[3]	彭超, 雷志锋, 张战刚, 何玉娟, 马腾, 蔡宗棋, 陈义强.中子辐射导致的SiC功率器件漏电增加特性研究. 必威体育下载 , 2023, 72(18): 186102.doi:10.7498/aps.72.20230976
[4]	张国帅, 尹超, 王兆繁, 陈泽, 毛世峰, 叶民友.中子辐照诱导钨再结晶的模拟研究. 必威体育下载 , 2023, 72(16): 162801.doi:10.7498/aps.72.20230531
[5]	李薇, 白雨蓉, 郭昊轩, 贺朝会, 李永宏.InP中子位移损伤效应的Geant4模拟. 必威体育下载 , 2022, 71(8): 082401.doi:10.7498/aps.71.20211722
[6]	郝蕊静, 郭红霞, 潘霄宇, 吕玲, 雷志锋, 李波, 钟向丽, 欧阳晓平, 董世剑.AlGaN/GaN高电子迁移率晶体管器件中子位移损伤效应及机理. 必威体育下载 , 2020, 69(20): 207301.doi:10.7498/aps.69.20200714
[7]	王铁山, 张多飞, 陈亮, 律鹏, 杜鑫, 袁伟, 杨迪.辐照导致硼硅酸盐玻璃机械性能变化. 必威体育下载 , 2017, 66(2): 026101.doi:10.7498/aps.66.026101
[8]	高云亮, 朱芫江, 李进平.Al辐照损伤初期的第一性原理研究. 必威体育下载 , 2017, 66(5): 057104.doi:10.7498/aps.66.057104
[9]	常晓阳, 尧舜, 张奇灵, 张杨, 吴波, 占荣, 杨翠柏, 王智勇.基于分布式布拉格反射器结构的空间三结砷化镓太阳能电池抗辐照研究. 必威体育下载 , 2016, 65(10): 108801.doi:10.7498/aps.65.108801
[10]	齐佳红, 胡建民, 盛延辉, 吴宜勇, 徐建文, 王月媛, 杨晓明, 张子锐, 周扬.电子辐照下GaAs/Ge太阳电池载流子输运机理研究. 必威体育下载 , 2015, 64(10): 108802.doi:10.7498/aps.64.108802
[11]	曾骏哲, 李豫东, 文林, 何承发, 郭旗, 汪波, 玛丽娅, 魏莹, 王海娇, 武大猷, 王帆, 周航.质子与中子辐照对电荷耦合器件暗信号参数的影响及其效应分析. 必威体育下载 , 2015, 64(19): 194208.doi:10.7498/aps.64.194208
[12]	谷文萍, 张林, 李清华, 邱彦章, 郝跃, 全思, 刘盼枝.中子辐照对AlGaN/GaN高电子迁移率晶体管器件电特性的影响. 必威体育下载 , 2014, 63(4): 047202.doi:10.7498/aps.63.047202
[13]	姜少宁, 万发荣, 龙毅, 刘传歆, 詹倩, 大貫惣明.氦、氘对纯铁辐照缺陷的影响. 必威体育下载 , 2013, 62(16): 166801.doi:10.7498/aps.62.166801
[14]	崔振国, 勾成俊, 侯氢, 毛莉, 周晓松.低能中子在锆中产生的辐照损伤的计算机模拟研究. 必威体育下载 , 2013, 62(15): 156105.doi:10.7498/aps.62.156105
[15]	朱勇, 李宝华, 谢国锋.质子对BaTiO3薄膜辐照损伤的计算机模拟. 必威体育下载 , 2012, 61(4): 046103.doi:10.7498/aps.61.046103
[16]	汪俊, 张宝玲, 周宇璐, 侯氢.金属钨中氦行为的分子动力学模拟. 必威体育下载 , 2011, 60(10): 106601.doi:10.7498/aps.60.106601
[17]	吴宜勇, 岳龙, 胡建民, 蓝慕杰, 肖景东, 杨德庄, 何世禹, 张忠卫, 王训春, 钱勇, 陈鸣波.位移损伤剂量法评估空间GaAs/Ge太阳电池辐照损伤过程. 必威体育下载 , 2011, 60(9): 098110.doi:10.7498/aps.60.098110
[18]	贺新福, 杨文, 樊胜.论FeCr合金辐照损伤的多尺度模拟. 必威体育下载 , 2009, 58(12): 8657-8669.doi:10.7498/aps.58.8657
[19]	范鲜红, 李敏, 尼启良, 刘世界, 王晓光, 陈波.Mo/Si多层膜在质子辐照下反射率的变化. 必威体育下载 , 2008, 57(10): 6494-6499.doi:10.7498/aps.57.6494
[20]	李养贤, 刘何燕, 牛萍娟, 刘彩池, 徐岳生, 杨德仁, 阙端鳞.中子辐照直拉硅中的本征吸除效应. 必威体育下载 , 2002, 51(10): 2407-2410.doi:10.7498/aps.51.2407

计量

文章访问数:4730
PDF下载量:157
被引次数:0

搜索

留言板