基于密度泛函理论, 采用第一性原理计算方法研究了C, N, O原子在金属V中的扩散行为. 首先, 讨论了C, N, O原子在V体心立方晶格中的间隙占位情况, 分析了其在间隙位置与V晶格的相互作用, 并探究了这种相互作用对金属V电子结构的影响. 研究结果表明: C, N, O原子在V的八面体间隙位置更为稳定, 并且C, N, O原子的2p电子与V的3d电子之间有比较强的成键作用; C, N, O原子的扩散势垒分别为0.89, 1.26, 0.98 eV, 并得出了其扩散系数表达式; 最后, 通过阿仑尼乌斯关系图对比了三者在V中扩散系数的大小, 并计算出体系温度在500–1100 K之间时其在V中的扩散系数, 计算结果与实验值基本符合.Based on the density functional theory, the diffusion behaviors of C, N and O atoms in V metal are studied by using the first-principles calculation method. Firstly, the site occupations of C, N and O atoms in the interstitials of the bcc V lattice are discussed. The interactions of interstitial C, N and O atoms with V lattice are analyzed, and the influence of the electronic structure on the interaction is explored. The study results show that C, N and O atoms are more stable in octahedral interstice of V metal, and a relatively strong bonding interaction is formed between their 2p-electron and the 3d-electron of V metal. The diffusion barriers of C, N and O atoms are 0.89 eV, 1.26 eV and 0.98 eV, respectively. Thus, the expressions of their diffusion coefficients are obtained. Finally, the diffusion coefficients of C, N and O atoms are compared by the Arrhenius plot. Their diffusion coefficients are calculated at 500-1100 K, and the calculation results are consistent with experimental values.
-
Keywords:
- V metal/
- first-principles/
- electronic structure/
- diffusion coefficient
[1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] [19] [20] [21] [22] [23] [24] [25] [26] [27] [28] [29] [30] [31] [32] [33] [34] -
[1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] [19] [20] [21] [22] [23] [24] [25] [26] [27] [28] [29] [30] [31] [32] [33] [34]
计量
- 文章访问数:8613
- PDF下载量:740
- 被引次数:0
下载: