采用新型双空穴注入层N, N, N', N'-tetrakis(4-Methoxy-phenyl)benzidine/Copper phthalocyanine(MeO-TPD/CuPc)及器件结构:ITO/MeO-TPD(15 nm)/CuPc(15 nm)/ N, N'-Bis(naphthalen-1-yl)-N, N'-bis(phenyl)benzidine (NPB, 15 nm)/8-hydroxyquinoline (Alq3, 50 nm)/LiF(1 nm)/Al(120 nm), 研制出高效有机发光二极管(器件D), 与其他器件(器件A, 没有空穴注入层的器件; 器件B, MeO-TPD单空穴注入层; 器件C, CuPc单空穴注入层)相比, 其性能得到明显改善. 器件D的起亮电压降至3.2 V, 比器件A, B, C的起亮电压分别降低了2, 0.3, 0.1 V. 器件D在10 V时, 其最大亮度为23893 cd/m2, 最大功率效率为1.91 lm/W, 与器件A, B, C的最大功率效率相比, 分别提高了43% (1.34 lm/W), 22% (1.57 lm/W), 7% (1.79 lm/W). 性能改善的主要原因是由于空穴注入和传输性能得到了改善, 通过单空穴型器件的J-V 曲线对这一现象进行了分析.Highly efficient organic light-emitting diode is fabricated with a novel double hole injection layer consisting of MeO-TPD/CuPc. We observe that the insertion of such a double hole injection layer leads to a striking enhancement in the electrical property:higher luminance, power efficiency and lower driving voltage. It has the configuration of ITO/MeO-TPD (15 nm)/CuPc(15 nm)/NPB(15 nm)/Alq3 (50 nm)/LiF(1 nm)/Al(120 nm). Its turn-on voltage is 3.2 V, which is 2, 0.3 and 0.1 V lower than those of the device without hole injection layer (device A) and the devices using MeO-TPD (device B), CuPc (device C) as hole injection layer, respctively. The highest luminance of the novel device reaches 23893 cd/m2 at a drving voltage of 10 V. The maximum power efficiency of the novel decive is 1.91 lm/W, which is 43% (1.34 lm/W), 22% (1.57 lm/W) and 7% (1.79 lm/W) higher than those of devices A, B and C, respectively. The improvement is ascribed to its high hole injection and transport ability. The results are verified by using the J-V curves of "hole-only" devices.
[1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] [19] [20] -
[1] [2] [3] [4] [5] [6] [7] [8] [9] [10] [11] [12] [13] [14] [15] [16] [17] [18] [19] [20]
计量
- 文章访问数:6458
- PDF下载量:705
- 被引次数:0
下载: