Fe基合金薄带的磁性能对应力敏感, 特别是退火过程应力感生磁各向异性是否可以用回火方法消除, 是一个令人感兴趣的科学问题. 本文采用同步辐射X射线衍射技术, 观测Fe _73.5Cu1Nb ₃Si _13.5B ₉非晶薄带经外加394.7 MPa应力540 ℃保温30 min退火后, 进行多次等温回火样品的微观结构, 用SupereyesB011型显微摄像机记录样品应力退火和回火过程的宏观伸长量, 并利用HP4294A型阻抗分析仪测量相应样品的磁各向异性. 对实验数据进行曲线拟合后发现, 虽然应力退火过程的残余应力引起的晶格各向异性是产生磁各向异性的主要原因, 但不是唯一原因, 在应力退火过程中非晶基底的蠕变引起的纳米晶晶粒定向团聚, 也是应力退火感生磁各向异性的重要原因; 而且, 因应力退火过程中非晶基底的蠕变引起纳米晶晶粒定向团聚感生的磁各向异性无法用等温回火方法完全消除.

关键词:

Abstract

The magnetic properties of Fe-based alloy ribbons are sensitive to stress, and it’s an interesting scientific question whether stress-induced magnetic anisotropy during annealing procedure can be eliminated by tempering. In this paper, the synchrotron radiation technique was used to observe the microstructure of Fe _73.5Cu1Nb ₃Si _13.5B ₉amorphous ribbons annealed at 540 ℃ for 30 minutes under 394.7MPa stress and tempered several times at the same temperature. The macroscopic elongation of the samples during stress annealing and tempering was recorded by SupereyesB011 microcamera, and the magnetic anisotropy of the samples was measured by HP4294A impedance analyzer. After fitting the experimental data, it is found that: (a) The lattice anisotropy, macroscopic strain and magnetic anisotropy of the sample show negative exponential attenuation with the tempering times, and their final residual are 19.04%. 98.27% and 31.65%. (b) Multiple tempering can not completely eliminate lattice anisotropy, macroscopic strain and magnetic anisotropy induced by stress annealing. (c) The magnetic anisotropy of the sample has a linear relationship with the lattice anisotropy, but the intercept between the reverse extension line of the relation curve and the longitudinal coordinate is not zero. When the lattice anisotropy is zero, there is still 16.36% magnetic anisotropy. This is different from Ohnuma's conclusion that lattice anisotropy is the direct cause of magnetic anisotropy. (d) The structure anisotropy caused by the residual stress after stress annealing is the main cause of magnetic anisotropy, but it is not the only reason. The directional congregation of agglomerated nanocrystalline grains caused by creep of amorphous substrates during stress annealing is also an important cause of magnetic anisotropy induced by stress annealing. Moreover, the magnetic anisotropy induced by the directional congregation of agglomerated nanocrystalline grains due to the creep of amorphous substrates during stress annealing can not be completely eliminated by tempering.

Keywords:

作者及机构信息

1.
2.
3.
4.

通信作者:方允樟,fyz@zjnu.cn

基金项目:国家重点基础研究发展计划(批准号: 2012CB825705)、浙江省重点研发计划项目(批准号: 2018C01G2031345)、浙江省自然科学基金(批准号: LY14A040003)和国家自然科学基金(批准号: 51771083)资助的课题.

Authors and contacts

1.
2.
3.
4.

Corresponding author:Fang Yun-Zhang,fyz@zjnu.cn

Funds:Project supported by the National Basic Research Program of China (Grant No. 2012CB825705), the Key Research Program of Zhejiang Province, China (Grant No. 2018C01G2031345), the Natural Science Foundation of Zhejiang Pvovince, China (Grant No. LY14A040003) and the National Natural Science Foundation of China (Grant No. 51771083).

文章全文: translate this paragraph

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]

施引文献

下载: 全尺寸图片幻灯片

	常数项	指数项	拟合优度
残余晶格各向异性$\alpha $/%	19.04	$80.93 \times {{\rm{e}}^{ - n/0.51}}$	0.99829
残余宏观应变$\delta $/%	98.27	$1.73 \times {{\rm{e}}^{ - n/0.48}}$	0.99913
残余磁各向异性$\gamma $/%	31.65	$68.30 \times {{\rm{e}}^{ - n/0.56}}$	0.99604

下载: 导出CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]

[1]	任延英, 李雅宁, 柳洪盛, 徐楠, 郭坤, 徐朝辉, 陈鑫, 高峻峰.过渡金属元素掺杂对磁铁矿磁矩及磁各向异性的调控. 必威体育下载 , 2024, 73(6): 066104.doi:10.7498/aps.73.20231744
[2]	樊晓筝, 李怡莲, 吴怡, 陈俊彩, 徐国亮, 安义鹏.二维磁性半导体笼目晶格Nb₃Cl₈单层的磁性及自旋电子输运性质. 必威体育下载 , 2023, 72(24): 247503.doi:10.7498/aps.72.20231163
[3]	张家滕, 徐吉元, 金佳莹, 孟睿阳, 董生智.晶界添加PrCu合金对(Pr, Nd, Dy)_32.2Co₁₃Cu_0.4Fe_balB_0.98M_1.05磁体磁性能与微观组织的影响. 必威体育下载 , 2022, 71(16): 167502.doi:10.7498/aps.71.20220406
[4]	卿煜林, 彭小莉, 胡爱元.自旋为1的双层平方晶格阻挫模型的相变. 必威体育下载 , 2022, 71(4): 047501.doi:10.7498/aps.71.20211685
[5]	孟婧, 冯心薇, 邵倾蓉, 赵佳鹏, 谢亚丽, 何为, 詹清峰.具有不同交换偏置方向的外延FeGa/IrMn双层膜的磁各向异性与磁化翻转. 必威体育下载 , 2022, 71(12): 127501.doi:10.7498/aps.71.20220166
[6]	张建强, 秦彦军, 方峥, 范晓珍, 杨慧雅, 邝富丽, 翟耀, 苗艳龙, 赵梓翔, 何佳俊, 叶慧群, 方允樟.Fe基合金应力感生不可逆磁各向异性机理. 必威体育下载 , 2022, 71(24): 247501.doi:10.7498/aps.71.20221509
[7]	杨雪, 杨青慧, 张怀武, 文岐业, 白飞明, 钟智勇, 张鼎, 黄建涛.面外取向的(BiTm)₃(GaFe)₅O₁₂磁光单晶薄膜制备及取向机理分析. 必威体育下载 , 2021, 70(10): 107801.doi:10.7498/aps.70.20202209
[8]	黄玉昊, 张贵涛, 王如倩, 陈乾, 王金兰.二维双金属铁磁半导体CrMoI₆的电子结构与稳定性. 必威体育下载 , 2021, 70(20): 207301.doi:10.7498/aps.70.20210949
[9]	刘祥, 米文博.Verwey相变处Fe₃O₄的结构、磁性和电输运特性. 必威体育下载 , 2020, 69(4): 040505.doi:10.7498/aps.69.20191763
[10]	文林, 胡爱元.双二次交换作用和各向异性对反铁磁体相变温度的影响. 必威体育下载 , 2020, 69(10): 107501.doi:10.7498/aps.69.20200077
[11]	卢启海, 唐晓莉, 宋玉哲, 左显维, 韩根亮, 闫鹏勋, 刘维民.氮化铁薄膜晶相合成热分析及其磁性. 必威体育下载 , 2019, 68(11): 118101.doi:10.7498/aps.68.20182195
[12]	姜兴东, 管兴胤, 黄娟娟, 范小龙, 薛德胜.N⁺注入修复外延Fe膜面内六重磁对称. 必威体育下载 , 2019, 68(12): 126102.doi:10.7498/aps.68.20190131
[13]	肖嘉星, 鲁军, 朱礼军, 赵建华.垂直磁各向异性L10-Mn1.67Ga超薄膜分子束外延生长与磁性研究. 必威体育下载 , 2016, 65(11): 118105.doi:10.7498/aps.65.118105
[14]	袁书强, 沈正祥, 周春华, 刘峰涛, 王芳, 杨辉, 陈炯.30CrMnSiNi2A晶格参量的测量及回复规律研究. 必威体育下载 , 2014, 63(3): 030702.doi:10.7498/aps.63.030702
[15]	陈家洛, 狄国庆.磁各向异性热电效应对自旋相关器件的影响. 必威体育下载 , 2012, 61(20): 207201.doi:10.7498/aps.61.207201
[16]	张辉, 曾德长.Tb0.3Dy0.7Fe2单晶中巨磁致伸缩的逆效应. 必威体育下载 , 2010, 59(4): 2808-2814.doi:10.7498/aps.59.2808
[17]	郭玉献, 王劼, 徐彭寿, 李红红, 蔡建旺.Co0.9Fe0.1薄膜面内元素分辨的磁各向异性. 必威体育下载 , 2007, 56(2): 1121-1126.doi:10.7498/aps.56.1121
[18]	施方也, 方允樟, 孙怀君, 郑金菊, 林根金, 吴锋民.应力退火Fe基纳米晶薄带横向磁各向异性的介观结构研究. 必威体育下载 , 2007, 56(7): 4009-4016.doi:10.7498/aps.56.4009
[19]	李锐鹏, 王　劼, 李红红, 郭玉献, 王锋, 胡志伟.软x射线磁性圆二色吸收谱研究铁单晶薄膜的面内磁各向异性. 必威体育下载 , 2005, 54(8): 3851-3855.doi:10.7498/aps.54.3851
[20]	林肇华, 戴道生.非晶态合金带中内应力场的形成和磁各向异性的分布. 必威体育下载 , 1982, 31(7): 871-881.doi:10.7498/aps.31.871

计量

文章访问数:6230
PDF下载量:44
被引次数:0

搜索

留言板